When webs weight increases, rupture strength, tearing strength and bursting strength are increased.

随着纤网定量的增加，断裂强度，撕破强度和顶破强度增加。

Results showed that sinter-HIP treatment can enhance the transverse rupture strength of WC-Co cemented carbides effectively.

结果表明：低压烧结工艺可以有效提高硬质合金的抗弯强度；

The hardness increased, but the density, transverse rupture strength and compressive strength decreased when prolonging the holding time.

随着球磨时间的延长，烧结合金的硬度升高，密度、横向断裂强度和压缩强度均下降。

The effects of milling time and sintering temperature on density, hardness, transverse rupture strength and compressive strength were mainly studied.

重点研究了球磨时间和烧结温度对烧结合金的密度、硬度、横向断裂强度和压缩强度的影响。

It was also found that at a fixed temperature the transverse-rupture strength of the alloy generally increased with the steepness of load-deflection curves.

还表明，在一定温度下，载荷-挠度曲线越陡，合金的抗弯强度一般也越高。